The customized Parking scribing raw materials from China manufacturer are generally normal temperature coatings. The normal temperature solvent paint is composed of synthetic resin (15% ~ 20%) to form a coating film and bond other raw materials. Including: pigments (15% ~ 20%) are mainly coloring and covering; Constitutional pigments (15% ~ 38%) are fillers to increase mechanical strength and wear resistance; Additives (2% ~ 5%) are ingredients that promote quick drying, prevent sedimentation, crust, easy dispersion and increase stability; The solvent (30% ~ 40%) gives the paint fluidity and adjusts the viscosity.

The customized Parking scribing raw materials from China manufacturer are composed of synthetic resin, coloring pigment, constitutional pigment, additive and solvent. The synthetic resin constitutes the coating film and promotes the adhesion of the raw materials. Pigments color and cover markings. The constitutional pigment is a filling material, which increases the mechanical strength and wear resistance of the coating. The additive can promote the quick drying of hot melt marking coating, prevent sedimentation, prevent scaling, easy dispersion and increase stability. The solvent (20% ~ 30%) gives the paint fluidity and adjusts the viscosity. The resin in the customized Parking scribing raw materials from China manufacturer must be thermoplastic, and it is required to have good compatibility with various substances, low acid value, light color, good heat resistance and weather resistance. The additives of hot-melt coating include plasticizer, anti settling agent, anti pollution agent and anti ultraviolet discoloration agent. If the customized Parking scribing raw materials from China manufacturer marks the line on the road, in order to increase the reflectivity of the line at night, it also premix glass beads and sprinkle glass beads on the surface. The process requirements of pavement marking coating shall comply with JT / T 280, GN 47 and GN 48.

 Characteristics of customized Parking scribing raw materials from China manufacturer

Strong adhesion: the resin content is reasonable, and the special rubber elastomer is added to the bottom oil, with strong adhesion. Ensure that the construction process is reasonable and no falling off occurs.

Good crack resistance: hot melt marking is easy to crack due to temperature difference. Add sufficient EVA resin to the coating to prevent cracking.

Bright color: the top coating pigment is adopted, with reasonable proportion and good weather resistance. Long term explosion without discoloration

High coating rate: small density, large volume and high coating rate are our main characteristics.

Good stain resistance: the quality and amount of PE wax are the key points affecting the stain resistance. 

Notes on construction process of customized Parking scribing raw materials from China manufacturer

1. Ensure that the working surface is clean and dry. It is recommended to construct at the temperature above 0 ℃ (for low-temperature construction, please increase the material temperature appropriately)

2. When the coating melts, the temperature shall be controlled between 180-220 ℃. After melting, it shall be fully stirred and evenly, and the material shall be discharged after 3-5 minutes of heat preservation, so as to fully reflect the performance of the hot-melt marking coating

3. The bottom oil treatment shall be sufficient, and the marking shall be applied after the bottom oil is completely dry. For the newly completed cement pavement, the construction shall be delayed for three months or the second bottom oil treatment shall be carried out as far as possible, otherwise the marking line may fall off.

4. For the newly completed cement pavement, the construction shall be delayed for three months or the second bottom oil treatment shall be carried out. Otherwise, the marking line may fall off

5. In the construction of sections with large traffic flow, please put warning caps after coating the bottom oil to prevent the wheels from rolling, taking away the bottom oil and leaving dust, otherwise some markings may fall off.